Composition containing chlorine, bromine and magnesium

ABSTRACT

A novel composition is provided which is suitable for use as a catalytic support which contains chlorine, bromine and magnesium. The molar ratio of bromine to chlorine is critical and ranges between about 1:99 to about 50:50, preferably between about 2.5:97.5 to about 20:80, and most preferably between about 2.5:97.5 to about 15:85. The molar ratio of magnesium to combined chlorine and bromine is not critical but generally ranges between about 1:1.6 and about 1:2.0, preferably between about 1:1.8 and about 1:2.0. The composition is obtained by reacting an organo magnesium compound with a mixture of chlorinated and brominated aluminum compounds.

CROSS-REFERENCES TO RELATED APPLICATIONS

Reference is made to applicants' following U.S. applications:

U.S. patent application Ser. No. 221,063, filed Dec. 29, 1980, entitled "Process for the Preparation of Aluminum Trihydrocarbyls".

U.S. patent application Ser. No. 221,200, filed Dec. 29, 1980, entitled "Olefin Polymerization Catalyst".

U.S. patent application Ser. No. 220,447, filed Dec. 29, 1980, entitled "Process for the Polymerization of Olefins."

FIELD OF THE INVENTION

The present invention relates to a novel composition containing magnesium, chlorine and bromine which is useful as a catalyst support. More particularly, this invention relates to such a composition obtained by reacting an organo magnesium compound with a mixture of chlorinated and brominated aluminum compounds.

DESCRIPTION OF THE PRIOR ART

It is well known in the art to use metallic catalysts to polymerize olefins such as ethylene, propylene, 1-butene and the like to form polymers of high molecular weight. One such general class of metallic catalyst are the "Ziegler-Natta" types consisting of aluminum alkyls or alkyl halides and titanium halides. Such catalysts polymerize olefins in a stereospecific manner resulting in the formation of olefin polymers which are characterized by high degrees of isotacticity and crystallinity.

U.S. Pat. No. 4,104,198 to May, Jr., et al discloses the reaction of ethyl aluminum sesquichloride with di(n-butyl)magnesium to form a precipitate, the treatment of a slurry of this precipitate with a solution containing 480 ppm Ti and tri-n-decyl aluminum to form a catalyst, and the use of this catalyst to polymerize ethylene. U.S. Pat. No. 4,163,831 to Gessell discloses the preparation of an olefin polymerization catalyst by reacting an organomagnesium compound with a metal halide such as an aluminum trihalide to form a finely divided intermediate reaction product and thereafter mixing the intermediate reaction product with a titanium compound. German Pat. No. 2643143 to Luciani et al discloses the preparation of an olefin polymerization catalyst by reacting (a) an organometallic aluminum compound devoid of halogen atoms directly linked to the aluminum atom, (b) an electron donor compound and (c) a solid component which is the reaction product of a halogenated magnesium compound with a tetravalent titanium compound and with an electron donor compound.

SUMMARY OF THE INVENTION

A novel composition has now been found which is suitable for use as a catalytic support. The composition contains chlorine, bromine and magnesium. The molar ratio of bromine to chlorine is critical and ranges between about 1:99 to about 50:50, preferably between about 2.5:97.5 to about 20:80, and most preferably between about 2.5:97.5 to about 15:85. The molar ratio of magnesium to combined chlorine and bromine is not critical but generally ranges between about 1:1.6 and about 1:2.0, preferably between about 1:1.8 and about 1:2.0. The composition is obtained by reacting an organo magnesium compound with a mixture of chlorinated and brominated aluminum compounds.

The term "organo magnesium compound" is intended to include divalent hydrocarbyl magnesium compounds wherein the hydrocarbyl portion thereof can be saturated or unsaturated, straight or branched chain alkyl radicals having from about one to about 24 carbon atoms, preferably from about one to about 10 carbon atoms; aryl radicals having from about six to about 20 carbon atoms, preferably from about six to about 10 carbon atoms; alkenyl radicals having from about one to about 30 carbon atoms, preferably from about one to about 20 carbon atoms; cycloalkyl radicals having from about three to about 40 carbon atoms, preferably from about three to about 30 carbon atoms; and aralkyl and alkaryl radicals having from about six to about 40 carbon atoms, preferably from about six to about 30 carbon atoms. The organo magnesium compound can be defined by the following formula:

    MgR.sup.1.sub.2.(AlR.sup.2.sub.2).sub.n

wherein n is an integer having a value of 0 or higher than 0 and preferably has a value of from 0 to 4, and each of R¹ and R² can be a hydrocarbyl radical as previously defined.

Specific examples of organo magnesium compounds that can be used include: diethylmagnesium, di-n-propylmagnesium, di-iso-propylmagnesium, di-n-butylmagnesium, di-sec-butylmagnesium, di-iso-butylmagnesium, di-hexylmagnesium, ethylbutylmagnesium, n-butyl-sec-butylmagnesium, diphenylmagnesium, dibenzylmagnesium, ditolylmagnesium, dicyclohexylmagnesium, magnesium aluminum pentaethyl, magnesium dialuminum octaethyl, magnesium aluminum diethyltriisobutyl, magnesium aluminum dibutyl hexaethyl, magnesium dialuminum diphenyl hexaethyl, magnesium dialuminum dibenzyl hexaethyl, magnesium dialuminum dicyclohexyl hexaethyl, magnesium dialuminum diethyl hexabutyl, etc. Of these the following organo magnesium compounds are preferred: diethylmagnesium, the dibutylmagnesiums, magnesium dialuminum octaethyl, magnesium aluminum pentaethyl, magnesium dialuminum diethyl hexa-isobutyl and magnesium dialuminum di-iso-butyl hexaethyl.

The chlorinated and brominated aluminum compounds that can be reacted with the organo magnesium compounds defined above can be defined by the following formula:

    Al(R.sup.3 R.sup.4 R.sup.5).sub.(3-a) X.sub.a

wherein each of R³, R⁴ and R⁵ can be a hydrocarbyl radical as defined above, X is chlorine or bromine, and a is an integer from 1 to 3. Specific examples of chlorinated and brominated aluminum compounds that can be used include: aluminum trichloride, aluminum ethyl dichloride, aluminum diethyl monochloride, aluminum isobutyl dichloride, aluminum di-isobutyl monochloride, aluminum diphenyl monochloride, aluminum dibenzyl monochloride, ethyl aluminum sesquichloride, aluminum n-butyl dichloride, aluminum di-n-butyl monochloride, aluminum sec-butyl dichloride, aluminum di-sec-butyl monochloride, aluminum propyl dichloride, aluminum dipropyl monochloride, etc. and the corresponding bromides. Of these the following chlorinated and brominated aluminum compounds are preferred: aluminum ethyl dichloride, aluminum diethyl monochloride, ethyl aluminum sesquichloride, aluminum dibutyl monochloride, aluminum butyl dichloride, etc. and the corresponding bromides, and aluminum tribromide.

When used as a catalytic support in the polymerization of olefins as hereinafter described, there are obtained high polymer yields and a high degree of isotacticity in the polymer product.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

In the reaction of the organo magnesium compounds with the chlorinated and brominated aluminum compounds, the molar ratios thereof can vary greatly as long as the molar ratios of chlorine and bromine in the final support will fall within the ranges previously defined above. For example, magnesium, chlorine and bromine can be employed in the reaction mixture in the molar range of about 1.0:1.0:0.02 to about 1.0:10.0:5.0, respectively.

In carrying out the reaction it is desirable to do so in the presence of an inert liquid diluent, preferably a hydrocarbon diluent, such as benzene, toluene, cyclohexane, heptane, etc. The amount of diluent used can vary over a wide range, but generally will be such that the resultant slurry will contain from about 70 to about 99 weight percent, preferably from about 90 to about 98 weight percent, of diluent based on the total weight of the slurry.

The reaction is simply effected by stirring the slurry and maintaining the temperature thereof in the range of about -20° to about 180° C., preferably about 25° to about 110° C., for about one minute to about 24 hours, preferably about one to about eight hours under any suitable inert atmosphere, such as nitrogen. The pressure, similarly, is not critical and ambient pressure is preferred, although pressures as low as about 25 millimeters of mercury or as high as about 100 pounds per square inch gauge (690 kPa), or even higher, can be used if desired.

The reaction mixture is then brought to ambient conditions of temperature and pressure and filtered. The recovered solids are then washed with a suitable hydrocarbon solvent, such as defined above, at ambient conditions, or in a temperature range of about 25° to about 100° C., until all the hydrocarbon-soluble constituents are removed therefrom. The solids are then dried to remove residual hydrocarbon therefrom. All of this is carried out in a suitable inert atmosphere. The solids so obtained constitute the novel composition of matter identified above containing substantially solely chlorine, bromine and magnesium suitable for use as a catalyst support.

The reactions described above can be exemplified by the following representative ideal equations: ##EQU1## wherein each of R', R", R'", and R"" can be a hydrocarbyl radical as previously defined, X can range from about 1.0 to about 1.98, preferably from about 1.6 to about 1.95, and most preferably from about 1.7 to about 1.95, and n is as previously defined.

In the reaction the aluminum compounds are removed from the process in the filtrate and by washing the solid residue after filtration with a hydrocarbon. An additional advantage of the present invention is that the aluminum hydrocarbyls prepared jointly with the novel magnesium halide supports can be recovered and used to treat the support for the subsequent polymerization of olefins as described hereinafter. The recovery of the desired aluminum hydrocarbyls can be effected in any conventional manner, for example, by subjecting the filtrate to distillation at a temperature within the range of about 50° to about 150° C. and a pressure of about 25 millimeters of mercury to about 760 millimeters of mercury to remove the solvent therefrom.

The novel composition of matter obtained herein will have a surface area of about 80 to about 250 square meters per gram, generally about 150 to about 200 square meters per gram.

In using the herein described composition of matter as a catalyst support, it is initially treated with any suitable electron donor compound (or Lewis base). Some examples of electron donor compounds which can be used are amines, amides, ethers, ketones, nitriles, phosphines, stibenes, arsines, phosphoramides, thioethers, thioesters, aldehydes, alcoholates, amides and salts of organic acids with metals of the groups I to IV of the periodic system of elements. Suitable organic acids include aromatic acids, as for example benzoic acid or p-hydroxybenzoic acid. Some examples of typical electron donor compounds include triethylamine, N,N'-dimethylpiperazine, diethylether, n-dibutyl ether, tetrahydrofuran, acetone, acetophenone, benzonitrile, tetramethyl urea, nitrobenzene, Libutylate, dimethylaminophenyl lithium and Na-dimethylamide. Preferred electron donor compounds include esters of acids containing organic and inorganic oxygen and ethers, such as n-dibutyl ether. Some of the most suitable esters are the alkyl esters of aromatic acids, such as benzoic acid, p-methoxy- or p-ethoxybenzoic acid and p-tolyl acid, e.g., ethyl benzoate, ethyl-p-methoxybenzoate, methyl-p-toluate and ethyl-p-butoxybenzoate. Further examples of suitable esters include diethylcarbonate, triethylborate, ethylpivalate, ethylnaphthoate, ethyl-o-chlorobenzoate, ethylacetate, dimethylmaleate, alkyl- or arylsilicate and methylmethacrylate. Treatment with the electron donor compound can be accomplished, for example, by suspending the novel composition (magnesium-chloride bromide) in the electron donor compound, alone or in the presence of an inert liquid hydrocarbon carrier, such as defined above, so that the novel composition will constitute, for example, from about 10 to about 50 weight percent of the resultant slurry. The slurry can be stirred, under an inert atmosphere, as defined above, for about 10 minutes to about six hours, or even longer, preferably for about 0.5 to about four hours, at a temperature of about 25° to about 150° C., preferably about 50° to about 100° C., after which the slurry is filtered and the recovered solids are dried under a vacuum. The dried solids are then mixed with titanium tetrachloride and the mixture can be heated, for example, for about 10 minutes to about six hours, preferably for about 0.5 to about four hours, at a temperature of about 50° to about 150° C., preferably about 80° to about 140° C. The resulting mixture is then filtered, preferably while warm, and the recovered solids are then washed with a hydrocarbon solvent, such as defined above, to remove hydrocarbon soluble material therefrom. The amount of titanium tetrachloride used is that amount that will result in a recovered solid product containing from about 0.3 to about three weight percent, preferably from about 0.7 to about 2.0 weight percent of titanium, calculated as elemental titanium. All of this is done in an inert atmosphere, as before.

In using the latter recovered solid product as a catalyst for the polymerization of alpha olefins, it is necessary to combine therewith an aluminum hydrocarbyl defined by the following formula:

    AlR.sup.6 R.sup.7 R.sup.8

wherein each of R⁶, R⁷ and R⁸ are hydrocarbyl radicals, as previously defined. Especially preferred aluminum hydrocarbyls for such use are triethylaluminum, tri-n-propylaluminum, tri-iso-propylaluminum, tri-n-butylaluminum and tri-iso-butylaluminum. As previously mentioned, the aluminum hydrocarbyls prepared jointly with the novel magnesium halide supports of this invention may be used in this step.

Prior to using the aluminum hydrocarbyl in the polymerization catalyst, it is necessary that it be contacted with an electron donor compound, such as defined above. The molar ratio of the aluminum hydrocarbyl to the electron donor compound can be, for example, in the range of about 0.1:1 to about 10:1, preferably about 0.5:1 to about 4:1. The treatment can be effected following the conditions outlined above in the treatment of the magnesium-chloride bromide compound with the electron donor compound. The treated aluminum hydrocarbyl is then mixed with the solid product previously obtained, such that the molar ratio of the aluminum hydrocarbyl to the titanium compound is in the range of about 0.1:1 to about 10:1, preferably about 0.5:1 to about 4:1. This can be accomplished by suspending the support, which has been treated with an electron donor compound and with titanium tetrachloride as previously described, in a solution containing the aluminum hydrocarbyl and the electron donor compound.

The resulting catalyst composition can be used to polymerize alpha olefins, preferably alpha olefins having at least three carbon atoms and most preferably alpha olefins containing from three to 10 carbon atoms. Examples include propylene, 1-butene, 4-methyl-1-pentene, 1-hexene, 1-octene, 1-decene, and the like. Copolymers of such alpha olefins with each other or with ethylene can also be obtained. The alpha olefin and catalyst are contacted with each other in a polymerization reactor at a temperature of about 25° to about 150° C., preferably about 40° to about 80° C., for about one-half to about five hours, preferably for about one to about three hours using a pressure that can range from about ambient to about 1200 pounds per square inch gauge (8274 kPa), preferably in the range of about 40 to about 600 pounds per square inch gauge (276 to 4137 kPa). The catalyst is preferably in suspension in a non-reactive hydrocarbon solvent, e.g., pentane, hexane, heptane, cyclopentane, cyclohexane, benzene, toluene, xylene, etc.

At the end of the polymerization period, the pressure is released, and the reaction product is filtered, washed with a solvent, such as isopropanol, and the solid polymers are recovered and then dried. The isotacticity of polymers resulting from the polymerization process defined above will be in excess of about 90 percent and will generally be in the range of about 97 to about 99 percent. The polymer yield using the defined catalyst will be in excess of about 55,000 grams per gram of titanium in the catalyst, generally will be in the range of about 65,000 to about 200,000, or even higher, grams of polymer per gram of titanium. The polymer particle diameter will be such that substantially all (above 99 percent) will have a particle diameter in excess of 90 microns. This means they can easily be handled and will be less susceptible to atmospheric oxidation.

The following examples illustrate the invention, and are not intended to limit the invention, but rather, are presented for purposes of illustration.

EXAMPLE I

Into a three-necked flask provided with a stirrer, dropping funnel and reflux condenser there was poured a Solution A which had been prepared by dissolving 0.18 mole of MgAl₂ (C₂ H₅)₈ in 500 milliliters of anhydrous n-heptane. A Solution B prepared by dissolving 0.24 mole of AlC₂ H₅ Cl₂ in 100 milliliters of anhydrous n-heptane was added to Solution A while stirring at room temperature, resulting in the immediate formation of a white Precipitate C. The reaction mixture was stirred while its temperature was raised to the boiling point of the solvent. At the end of six hours the flask was cooled to room temperature and the Precipitate C was recovered by filtration, washed with anhydrous n-heptane and dried under vacuum. Seventeen grams of insoluble Precipitate C were recovered having a surface area of 150 m² /gram and was found to contain 24.2 weight percent magnesium, 0.6 weight percent aluminum and 65.3 weight percent chlorine.

Precipitate C (1.1 grams) was suspended in a solution consisting of four milliliters of anhydrous n-heptane and one milliliter of ethylbenzoate and the suspension was heated, while stirring, to 70° C. and maintained at such temperature for four hours. The mixture was filtered and the recovered solids were washed with 10 milliliters of n-heptane and dried. To the solids there were added 10 milliliters of TiCl₄ and the temperature of the resulting mixture was raised to the boiling point (about 140° C.) while stirring. After three hours the temperature was lowered to 100° C., the excess TiCl₄ was removed from the mixture by filtration and the recovered Insoluble Material D was washed three times with anhydrous n-heptane and dried under vacuum. The Insoluble Material D (1.27 grams) was found to contain 18.9 weight percent magnesium, 0.65 weight percent aluminum, 1.4 weight percent titanium and 53.8 weight percent chlorine.

Insoluble Material D (0.1 gram) was suspended in a solution containing 500 milliliters of anhydrous n-heptane, 0.6 milliliters of Al(C₂ H₅)₃ and 0.3 milliliters of ethyl anisate. The suspension was transferred under vacuum into a one-liter autoclave, thermostatted at 50° C. and propylene was then fed to the reactor, while the contents were stirred, until a pressure of 90 pounds per square inch (621 kPa) was reached. This pressure was maintained for one hour, after which propylene feed was discontinued, the autoclave was cooled to room temperature and the unreacted propylene was vented. The contents of the autoclave were poured into two liters of isopropanol and, after filtration and drying, 45 grams of isotactic polypropylene were recovered. There were obtained from the polymerization slurry 32,143 grams of propylene polymer per gram of titanium in the catalyst. Ninety-six percent of the polymer was found to be insoluble in boiling n-heptane. The intrinsic viscosity [n] (in tetralin at 135° C.) was equal to 3.9 deciliters/gram. All of the reactions, escept for recovery of the polymer, were performed in a nitrogen atmosphere.

EXAMPLE II

The procedure of Example I was followed except that Solution A consisted of 0.04 mole of MgAl₂ (C₂ H₅)₆ -(C₄ H₉)₂ dissolved in 200 milliliters of anhydrous n-heptane, Solution B consisted of 0.12 mole of Al(C₂ H₅)₂ Cl in 70 milliliters of anhydrous n-heptane and Precipitate C was treated for two hours with a solution of 0.3 milliliter of ethyl benzoate and five milliliters of n-heptane at boiling temperature (about 98° C.) for two hours and dried under vacuum without washing before the treatment with TiCl₄. Starting with one gram of Precipitate C, 0.95 gram of Insoluble Material D was recovered which was found to contain 20.3 weight percent magnesium, 0.36 weight percent aluminum, 1.0 weight percent titanium and 57 weight percent chlorine. The polymer yield in this run was 53 grams, with 53,000 grams of polypropylene being obtained per gram of titanium. The intrinsic viscosity of the polymer was 4.3 deciliters per gram and 95 percent was insoluble in boiling n-heptane.

EXAMPLE III

The same procedure as in the following Example IV was followed except that Solution A contained 0.03 mole of Mg(C₄ H₉)₂ and Solution B contained 0.058 mole of Al(C₂ H₅)₂ Cl and 0.0005 mole of AlBr₃. There were recovered three grams of Precipitate C. Insoluble Material D (0.97 gram) was prepared starting with one gram of Precipitate C. In the polymerization 62 grams of polypropylene were obtained. The intrinsic viscosity of the polymer was 4.9 deciliters per gram and 98 percent was insoluble in boiling n-heptane.

EXAMPLE IV

The same procedure was used as in Example II except that Solution A contained 0.03 mole of MgAl₂ (C₂ H₅)₈ in 150 milliliters of n-heptane and Solution B contained 0.056 mole of Al(C₂ H₅)₂ Cl and 0.002 mole of AlBr₃ in 50 milliliters of n-heptane. There were recovered three grams of Precipitate C which was found to contain 20 weight percent magnesium, 0.1 weight percent aluminum, 47.3 weight percent chlorine and 13.1 weight percent bromine. Insoluble Material D (0.84 gram) was recovered starting with 0.95 gram of Precipitate C. Insoluble Material D was found to contain 20.7 weight percent magnesium, 0.05 weight percent aluminum, 0.8 weight percent titanium, 9.7 weight percent bromine and 53.2 weight percent chlorine. The polymer yield amounted to 90 grams. There were obtained 112,500 grams of polypropylene polymer per gram of titanium. The intrinsic viscosity was 3.7 deciliters per gram and 97 percent was insoluble in boiling n-heptane.

EXAMPLE V

The same procedure was used as in Example IV except that Solution A contained 0.03 mole of Mg(C₄ H₉)₂ instead of MgAl₂ (C₂ H₅)₈. There were recovered 3.18 grams of Precipitate C which was found to contain 20 weight percent magnesium, 0.4 weight percent aluminum, 13 weight percent bromine and 51.7 weight percent chlorine. Insoluble Material D (0.96 gram) was obtained starting with one gram of Precipitate C. It was found to contain 18.4 weight percent magnesium, 0.1 weight percent aluminum, 1.5 weight percent titanium and 56.4 weight percent chlorine. There were recovered 100 grams of polypropylene polymer. This amounted to 66,667 grams of polymer per gram of titanium in the catalyst. The intrinsic viscosity of the polymer was 3.8 deciliters per gram and 97 percent was insoluble in boiling n-heptane.

EXAMPLE VI

The procedure of Example IV was followed except that Solution A contained 0.03 mole of Mg(C₄ H₉)₂ and Solution B contained 0.049 mole of Al(C₂ H₅)₂ Cl, 0.004 mole of AlBr₃ and 0.037 mole of Al(C₂ H₅)₃. Precipitate C (3.7 grams) was recovered. Insoluble Material D (0.93 gram) was obtained starting with 0.93 gram of Precipitate C. The polypropylene obtained amounted to 55 grams. The intrinsic viscosity of the polymer was 4.4 deciliters per gram and 98 percent was insoluble in boiling n-heptane.

EXAMPLE VII

The procedure of Example IV was again followed except that Solution A contained 0.03 mole of MgAl₂ -(C₂ H₅)₆ (C₄ H₉)₂ and Solution B contained 0.03 mole of Al(C₂ H₅)₂ Cl and 0.016 mole of AlC₂ H₅ Br₂. Precipitate C (4.2 grams) was obtained. Starting with one gram of Precipitate C there was recovered 0.74 gram of Insoluble Material D, which was found to contain 18.6 weight percent magnesium, 0.12 weight percent aluminum, 1.5 weight percent titanium, 17.9 weight percent bromine and 44.8 weight percent chlorine. There were recovered 45 grams of polypropylene. This amounted to 30,000 grams of polymer per gram of titanium. The intrinsic viscosity of the polymer was 3.8 deciliters per gram and 95 percent was insoluble in boiling heptane.

EXAMPLE VIII

In this example the procedure of Example II was followed except that Solution A contained 0.045 mole of MgAl₂ (C₂ H₅)₈ and Solution B contained 0.045 mole of Al(C₂ H₅)₂ Br dissolved in 50 milliliters of n-heptane. There were recovered 4.3 grams of Precipitate C which was found to contain 12.8 weight percent magnesium, 0.36 weight percent aluminum and 80.5 weight percent bromine. Two grams of Precipitate C were used to obtain 1.7 grams of Insoluble Material D which was found to contain 12.65 weight percent magnesium, 0.1 weight percent aluminum, 1.0 weight percent titanium, 58.4 weight percent bromine and 11.0 weight percent chlorine. The polymer yield was 45 grams. There were obtained 45,000 grams of polypropylene polymer per gram of titanium. The intrinsic viscosity was 3.0 deciliters per gram and 89.0 percent of the polymer was insoluble in boiling n-heptane.

The data above are tabulated below in Table I.

                                      TABLE I                                      __________________________________________________________________________                                             Intrinsic                              Support            Polymer Yield,                                                                         Polymer Yield,                                                                         Isotac-                                                                             Viscosity,                                  Molar                                                                              Molar Ratio, Mag-                                                                        Grams Polymer                                                                          Grams Polymer                                                                          ticity                                                                              Deciliters                                  Ratio,                                                                             nesium to Combined                                                                       Per Gram of                                                                            Per Gram of                                                                            Weight                                                                              Per Gram                               Example                                                                             Br:Cl                                                                              Cl and Br Total Catalyst                                                                         Titanium                                                                               Percent*                                                                            (ASTM D-2857)                          __________________________________________________________________________     I     0:100                                                                             1:1.84    450     32,143  96   3.9                                    II    0:100                                                                             Not taken 530     53,000  95   4.3                                    III   3:97                                                                              Not taken 620     Not taken                                                                              98   4.9                                    IV   12:88                                                                              1:1.82    900     112,500 97   3.7                                    V    11:89                                                                              1:1.98    1000    66,667  97   3.8                                    VI   24:76                                                                              Not taken 550     Not taken                                                                              98   4.4                                    VII  52:48                                                                              Not taken 450     30,000  95   3.8                                    VIII 100:00                                                                             1:1.90    450     45,000  89   3.0                                    __________________________________________________________________________      *Weight of polymer insoluble in boiling nheptane                         

In the above table it can be seen that the results obtained using the supports of Examples III to VI are far better than when chlorine is the only halogen in the support (Examples I and II) or when bromine is the only halogen in the support (Example VIII) or when the molar ratio of bromine to chlorine is outside the critical ratio (Example VII).

That it is critical that the novel composition suitable for use as a catalyst support containing chlorine, bromine and magnesium in the defined amounts be obtained by reacting an organo magnesium compound with a mixture of chlorinated and brominated aluminum compounds is apparent from the following.

EXAMPLE IX

The procedure of Example IV was followed, except that Precipitate C (the halogenated magnesium compound) was obtained by disproportionating an intimate mixture containing 0.007 mole (0.93 gram) of MgC₂ H₅ Br and 0.08 mole (7.10 gram) of MgC₂ H₅ Cl with Al(C₂ H₅)₃ according to the general procedure described by K. Ziegler and E. Holzkamp in Ann. Chem., 605 (1957) 93. The resulting product was washed with anhydrous n-heptane and dried in vacuuo. One gram of Insoluble Material D was prepared starting with one gram of Precipitate C. The elemental analysis of Insoluble Material D was as follows: 18.7 weight percent magnesium, 0.05 weight percent aluminum, 1.3 weight percent titanium, 6.6 weight percent bromine and 53.9 weight percent chlorine. The molar ratio of bromine to chlorine was 5:95. The amount of polymer obtained was 15 grams. This amounted to 11,538 grams of polypropylene per gram of titanium. The intrinsic viscosity of the polymer was 3.5 deciliters per gram and only 87 percent was found to be insoluble in hot n-heptane.

Although the invention has been described in considerable detail with particular reference to certain preferred embodiments thereof, variations and modifications can be effected within the spirit and scope of the invention as described hereinbefore, and as defined in the appended claims. 

We claim:
 1. A novel composition suitable for use as a catalyst support containing chlorine, bromine and magnesium wherein the molar ratio of bromine to chlorine ranges between about 1:99 to about 50:50 obtained by reacting an organo magnesium compound with a mixture of chlorinated and brominated aluminum compounds.
 2. A composition as defined in claim 1 wherein the molar ratio of magnesium to combined chlorine and bromine ranges between about 1:1.6 to about 1:2.0.
 3. A composition as defined in claim 1 wherein said organo magnesium compound is a divalent hydrocarbyl magnesium compound wherein the hydrocarbyl portion thereof is a radical selected from the group consisting of alkyl radicals having from about one to about 24 carbon atoms, aryl radicals having from about six to about 20 carbon atoms, alkenyl radicals having from about one to about 30 carbon atoms, cycloalkyl radicals having from about three to about 40 carbon atoms, and aralkyl and alkaryl radicals having from about six to about 40 carbon atoms.
 4. A composition as defined in claim 3 wherein said organo magnesium compound is selected from the group consisting of diethylmagnesium, di-n-propylmagnesium, di-iso-propylmagnesium, di-n-butylmagnesium, di-sec-butylmagnesium, di-iso-butylmagnesium, di-hexylmagnesium, ethylbutylmagnesium, n-butyl-sec-butylmagnesium, diphenylmagnesium, dibenzylmagnesium, ditolylmagnesium, dicyclohexylmagnesium, magnesium aluminum pentaethyl, magnesium dialuminum octaethyl, magnesium aluminum diethyltriisobutyl, magnesium aluminum dibutyl hexaethyl, magnesium dialuminum diphenyl hexaethyl, magnesium dialuminum dibenzyl hexaethyl, magnesium dialuminum dicyclohexyl hexaethyl and magnesium dialuminum diethyl hexabutyl.
 5. A composition as defined in claim 1 wherein said chlorinated and brominated aluminum compounds have the formula:

    Al(R.sup.3 R.sup.4 R.sup.5).sub.(3-a) X.sub.a,

wherein each of R³, R⁴, and R⁵ is a hydrocarbyl radical selected from the group consisting of alkyl radicals having from about one to about 24 carbon atoms, aryl radicals having from about six to about 20 carbon atoms, alkenyl radicals having from about one to about 30 carbon atoms, cycloalkyl radicals having from about three to about 40 carbon atoms, and aralkyl and alkaryl radicals having from about six to about 40 carbon atoms, X is chlorine or bromine and a is an integer from 1 to
 3. 6. A composition as defined in claim 5 wherein said chlorinated and brominated aluminum compounds are selected from the group consisting of aluminum trichloride, aluminum ethyl dichloride, aluminum diethyl monochloride, aluminum isobutyl dichloride, aluminum di-isobutyl monochloride, aluminum diphenyl monochloride, aluminum dibenzyl monochloride, ethyl aluminum sesquichloride, aluminum n-butyl dichloride, aluminum di-n-butyl monochloride, aluminum sec-butyl dichloride, aluminum di-sec-butyl monochloride, aluminum propyl dichloride, aluminum dipropyl monochloride, and the corresponding bromides.
 7. A composition as defined in claim 1 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 8. A composition as defined in claim 1 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 9. A composition as defined in claim 2 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 10. A composition as defined in claim 2 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 11. A composition as defined in claim 4 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 12. A composition as defined in claim 4 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 13. A composition as defined in claim 6 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 14. A composition as defined in claim 6 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 15. A composition as defined in claim 1 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 16. A composition as defined in claim 2 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 17. A composition as defined in claim 4 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 18. A composition as defined in claim 6 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 19. A composition as defined in claim 1 wherein said compounds are combined in an inert diluent to form a slurry.
 20. A composition as defined in claim 2 wherein said compounds are combined in an inert diluent to form a slurry.
 21. A composition as defined in claim 4 wherein said compounds are combined in an inert diluent to form a slurry.
 22. A composition as defined in claim 6 wherein said compounds are combined in an inert diluent to form a slurry.
 23. A composition as defined in claim 19 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 24. A composition as defined in claim 19 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours.
 25. A composition as defined in claim 20 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 26. A composition as defined in claim 20 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours.
 27. A composition as defined in claim 21 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 28. A composition as defined in claim 21 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours.
 29. A composition as defined in claim 22 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 30. A composition as defined in claim 22 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours.
 31. A process for preparing a novel composition suitable for use as a catalyst support containing chlorine, bromine and magnesium which comprises reacting an organo magnesium compound with a mixture of chlorinated and brominated compounds, said chlorinated and brominated compounds being present in said mixture in amounts sufficient to provide in said composition a molar ratio of bromine to chlorine in the range between about 1:99 to about 50:50.
 32. A process as defined in claim 31 wherein the molar ratio of magnesium to combined chlorine and bromine in the final composition ranges between about 1:1.6 to about 1:2.0.
 33. A process as defined in claim 31 wherein said organo magnesium compound is a divalent hydrocarbyl magnesium compound wherein the hydrocarbyl portion thereof is a radical selected from the group consisting of alkyl radicals having from about one to about 24 carbon atoms, aryl radicals having from about six to about 20 carbon atoms, alkenyl radicals having from about one to about 30 carbon atoms, cycloalkyl radicals having from about three to about 40 carbon atoms, and aralkyl and alkaryl radicals having from about six to about 40 carbon atoms.
 34. A process as defined in claim 33 wherein said organo magnesium compound is selected from the group consisting of diethylmagnesium, di-n-propylmagnesium, di-iso-propylmagnesium, di-n-butylmagnesium, di-sec-butylmagnesium, di-iso-butylmagnesium, di-hexylmagnesium, ethylbutylmagnesium, n-butyl-sec-butylmagnesium, diphenylmagnesium, dibenzylmagnesium, ditolylmagnesium, dicyclohexylmagnesium, magnesium aluminum pentaethyl, magnesium dialuminum octaethyl, magnesium aluminum diethyltriisobutyl, magnesium aluminum dibutyl hexaethyl, magnesium dialuminum diphenyl hexaethyl, magnesium dialuminum dibenzyl hexaethyl, magnesium dialuminum dicyclohexyl hexaethyl and magnesium dialuminum diethyl hexabutyl.
 35. A process as defined in claim 31 wherein said chlorinated and brominated aluminum compounds have the formula:

    Al(R.sup.3 R.sup.4 R.sup.5).sub.(3-a) X.sub.a,

wherein each of R³, R⁴, and R⁵ is a hydrocarbyl radical selected from the group consisting of alkyl radicals having from about one to about 24 carbon atoms, aryl radicals having from about six to about 20 carbon atoms, alkenyl radicals having from about one to about 30 carbon atoms, cycloalkyl radicals having from about three to about 40 carbon atoms, and aralkyl and alkaryl radicals having from about six to about 40 carbon atoms, X is chlorine or bromine and a is an integer from 1 to
 3. 36. A process as defined in claim 35 wherein said chlorinated and brominated aluminum compounds are selected from the group consisting of aluminum trichloride, aluminum ethyl dichloride, aluminum diethyl monochloride, aluminum isobutyl dichloride, aluminum di-isobutyl monochloride, aluminum diphenyl monochloride, aluminum dibenzyl monochloride, ethyl aluminum sesquichloride, aluminum n-butyl dichloride, aluminum di-n-butyl monochloride, aluminum sec-butyl dichloride, aluminum di-sec-butyl monochloride, aluminum propyl dichloride, aluminum dipropyl monochloride, and the corresponding bromides.
 37. A process as defined in claim 31 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 38. A process as defined in claim 31 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 39. A process as defined in claim 32 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 40. A process as defined in claim 32 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 41. A process as defined in claim 34 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 42. A process as defined in claim 34 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 43. A process as defined in claim 36 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 20:80.
 44. A process as defined in claim 36 wherein the molar ratio of bromine to chlorine ranges between about 2.5:97.5 to about 15:85.
 45. A process as defined in claim 31 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 46. A process as defined in claim 32 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 47. A process as defined in claim 34 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 48. A process as defined in claim 36 wherein the molar ratios of magnesium to chlorine to bromine compounds which are combined ranges between about 1.0:1.0:0.2 to about 1.0:10.0:5.0.
 49. A process as defined in claim 31 wherein said compounds are combined in an inert diluent to form a slurry.
 50. A process as defined in claim 32 wherein said compounds are combined in an inert diluent to form a slurry.
 51. A process as defined in claim 34 wherein said compounds are combined in an inert diluent to form a slurry.
 52. A process as defined in claim 36 wherein said compounds are combined in an inert diluent to form a slurry.
 53. A process as defined in claim 49 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 54. A process as defined in claim 49 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours.
 55. A process as defined in claim 50 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 56. A process as defined in claim 50 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours.
 57. A process as defined in claim 51 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 58. A process as defined in claim 51 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours.
 59. A process as defined in claim 52 wherein said slurry is maintained at a temperature in the range of about -20° C. to about 180° C. for about one minute to about 24 hours.
 60. A process as defined in claim 52 wherein said slurry is maintained at a temperature in the range of about 25° to about 110° C. for about one to about eight hours. 